The Fluoride Fibers in Stock
|
|
|
|
|
|
|
|
Single
Mode ZBLAN Fibers in Stock |
|
|
| Item |
Dopant |
Concent
ration
ppm mol |
Core dia.
µm |
Cladding dia.
µm |
Coating dia.
µm |
Cut-off
nm |
Loss
dB/m@nm |
| ZSF-3.1/123-0.68T |
Tm |
680 |
3.1±0.3 |
123±3 |
450±30 |
<1380 |
<0.05@1400 |
| ZSF-3.6/123-4.4T |
Tm |
4400 |
3.6±0.3 |
123±3 |
450±30 |
<1400 |
<0.1@1301 |
|
|
|
|
|
|
|
|
Multi Mode ZBLAN Fibers in Stock
|
|
|
| Item |
NA |
Core dia.
µm |
Cladding dia.
µm |
Coating dia.
µm |
Loss
dB/m@nm |
| ZMF-160/200 |
0.27±0.02 |
160±10 |
200±10 |
450±30 |
<0.1@2500 |
| ZMF-400/500 |
0.27±0.02 |
400±25 |
500±25 |
600±30 |
<0.1@2500 |
|
|
|
|
|
|
|
|
Double Cladding ZBLAN Fibers in Stock |
|
|
| Item |
Dopant |
Concent
ration
ppm mol |
Core dia.
µm |
1st Cladding
configuration
µm |
2ndCladd
ing dia.
µm |
| ZDF-14/300-40E-D |
Er |
40,000 |
14±3 |
300/D shape |
400±10 |
| ZDF-70/250-60E-C |
Er |
60,000 |
70±11 |
250/Circular |
400±10 |
| ZDF-52/250-60E-C |
Er |
60,000 |
52±6 |
250/Circular |
400±10 |
| ZDF-33/250-60E-C |
Er |
60,000 |
33±5 |
250/Circular |
400±10 |
| ZDF-34/350-60E-D |
Er |
60,000 |
34±5 |
350/D shape |
480±10 |
| ZDF-23/350-60E-D |
Er |
60,000 |
23±3 |
350/D shape |
430±10 |
| ZDF-15/350-60E-D |
Er |
60,000 |
15±3 |
350/D shape |
430±10 |
| ZDF-17/200x250-60E-R |
Er |
60,000 |
17±5 |
200x250/Rectangular |
365±10 |
| ZDF-9/125-13.7T-C |
Tm |
13,700 |
9±1 |
125 Circular |
200±10 |
|
|
|
Note: 2nd cladding
is flurorine-contained resin. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
.gif)
.gif){kind=small}
.gif){kind=small}